產(chǎn)品詳情
| 類似或等效規(guī)格 | |||||||||||||
| CDA ASTM SAE AMS Federa Military Other | |||||||||||||
| C91600 | B427 | QQ-C-390,F1 | |||||||||||
| 化學成分 | |||||||||||||
| Cu(%) | Pb (%) | Sn(%) | Zn (%) | Fe (%) | P (%) | Ni (%)2 | AL(%) | S(%) | Sb (%) | Si(% | |||
| 86.00-89.00 | 0.25 | 9.70-10.80 | 0.25 | 0.20 | 0.30 | 1.20-2.00 | 0.005 | 0.05 | 0.20 | 0.005 | |||
| 機械性能 | |||||
| 抗拉強度,min | 屈服強度，負載下延伸0.5%時,min |
Elongation,in 2 in or 50 mm,min |
Brinell hardness (500 kg load) |
||
 ksi MPa MPa % typical BHN
|
|||||
| 45 | 310 | 25 | 172 | 10 | 85 |
| 物理性質(zhì) | ||
| US customary | Metric | |
| 熔點-液相線 | 1887'F | 1031'C |
| 熔點-固相線 | 1575"F | 857"C |
| 密度 | 0.32 lb/in3at 68"F | 8.86gm/cm3at20°℃ |
| 比重 | 8.86 | 8.86 |
| 電導率 | 10%IACS at 68°F | 0.058 MegaSiemens/cm at 20"℃ |
| 電導率 | 40.8 Btu/sq ft/ft hr/F at 68°F | 70.6W/m at 20°C |
| 熱膨脹系數(shù)68-392 | 9 ·10-6 per'F(68-392"F) | 15.5 ·10-+per'C(20-200"C) |
| 比熱容量 | 0.09 Btu/lb/'Fat 68"F | 3771J/kg at 20°℃ |
| 拉伸彈性模量 | 16000 ksi | 110000 MPa |
C91600 錫青銅棒的性能特點
C91600 錫青銅棒是一種高性能的銅合金材料，具有以下顯著的性能特點：
高強度：C91600 錫青銅棒具有較高的抗拉強度和屈服強度，能夠承受較大的載荷和應(yīng)力，使其在機械零部件等領(lǐng)域表現(xiàn)出色5。
良好的耐磨性：這一特性使得它在需要耐磨的場合，如滑動軸承、耐磨部件等，能夠長時間穩(wěn)定運行，減少磨損和更換頻率11。
耐海水腐蝕性能：由于其成分中高銅和錫含量，以及適量的鎳和鋁等元素，C91600 錫青銅棒在海洋環(huán)境中表現(xiàn)出優(yōu)異的耐蝕性，適用于船舶零部件和海洋結(jié)構(gòu)件等2。
優(yōu)良的耐蝕性：能夠在多種腐蝕介質(zhì)中保持穩(wěn)定，特別在惡劣的環(huán)境條件下，依然能夠保持良好的性能，延長使用壽命9。
良好的韌性：具備一定的韌性，使其在受到?jīng)_擊和振動時不易斷裂，增加了其在復雜工況下的可靠性6。
C91600 錫青銅棒的用途
C91600 錫青銅棒具有廣泛的用途，主要包括以下幾個方面：
海洋工程：常用于制造船舶零部件，如螺旋槳、閥門、海洋結(jié)構(gòu)件等，其出色的耐海水腐蝕性能能夠確保在海洋環(huán)境中的長期穩(wěn)定運行10。
電氣工程：可用于制造電氣接觸材料和導體，因其良好的導電性和耐蝕性，能夠保障電氣系統(tǒng)的穩(wěn)定和安全運行4。
機械制造：適用于制造強度比較高的螺桿、螺帽、銅套、密封環(huán)等零件，以及需要耐磨部件的地方，如軸承、齒輪等，滿足機械系統(tǒng)的高強度和耐磨需求11。
精密儀器：由于其良好的機加工性能和穩(wěn)定的物理化學性質(zhì)，可用于制造各種精密儀器的零部件，保證儀器的精度和可靠性