ENAW Al Mn1Cu鋁合金。薄板、帶材
|
|
|
|
|
|
|
|
編號：ENAW-3003
|
|
|
|
|
|
|
|
分類：鋁-3000系列（錳錳是主要合金元素）
|
|
|
|
|
|
|
|
密度2.73 g/cm3
|
|
|
|
|
|
|
|
標準：EN 573-3:2009鋁和鋁合金。鍛造產(chǎn)品的化學成分和形式。產(chǎn)品的化學成分和形式
|
|
|
|
|
|
|
|
EN 755-2:2008鋁和鋁合金。擠壓棒材、管材和型材。機械性能
|
|
|
|
|
|
|
|
EN 485-2:2008鋁和鋁合金。薄板、帶材和板材。機械性能
|
|
|
|
|
|
|
|
EN 754-2:2008鋁和鋁合金。冷拔棒材/棒材和管材。機械性能
|
|
|
|
|
|
|
|
EN 546-2:1997鋁和鋁合金。箔機械性能
|
|
|
|
|
|
|
|
EN 683-2:2006鋁和鋁合金。Finstock。機械性能
|
|
|
|
|
|
|
|
EN 1301-2:1997鋁和鋁合金。拉線。機械性能
|
|
|
|
|
|
|
|
EN 851:1996鋁和鋁合金。用于生產(chǎn)烹飪用具的圓形和圓形原料。規(guī)格
|
|
|
|
|
|
|
|
EN 941:1996鋁和鋁合金。用于一般應用的圓形和圓形坯料。規(guī)格
|
|
|
|
|
|
|
|
EN 1386:2007鋁和鋁合金。踏板。規(guī)格
|
|
|
|
|
|
|
|
EN 1396:2007鋁和鋁合金。一般應用的卷材涂層片材和帶材。規(guī)格
|
|
|
|
|
|
|
|
EN 12392:2000鋁和鋁合金。鍛造產(chǎn)品。壓力設備生產(chǎn)用產(chǎn)品的特殊要求
|
|
|
|
|
|
|
|
EN 570:2007鋁和鋁合金。從鍛造產(chǎn)品中獲得的沖擊擠壓坯料。規(guī)格
|
|
|
|
|
|
|
|
EN 1715-3：2008鋁和鋁合金。提取庫存。機械用途的具體要求（不包括焊接）
|
|
|
|
|
|
|
|
Chemical comb % of grade ENAW-AlMn1Cu ( ENAW-3003 )
|
|
|
|
|
|
|
|
Fe
|
Si
|
Mn
|
Cu
|
Zn
|
Others
|
-
|
|
max 0.7
|
max 0.6
|
1 - 1.5
|
0.05 - 0.2
|
max 0.1
|
each 0.05; total 0.15
|
Al - remainder
|
|
|
|
|
|
|
|
|
|
Mechanical properties of grade ENAW-AlMn1Cu ( ENAW-3003 )
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rm - Tensile strength (MPa) (O)
|
95-135
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rm - Tensile strength (MPa) (H12)
|
120-160
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rm - Tensile strength (MPa) (H14)
|
145-185
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rm - Tensile strength (MPa) (O) (H111)
|
95-135
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rm - Tensile strength (MPa) (F) (H112)
|
95
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rp0.2 0.2% proof strength (MPa) (O)
|
35
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rp0.2 0.2% proof strength (MPa) (H12)
|
90
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rp0.2 0.2% proof strength (MPa) (H14)
|
125
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rp0.2 0.2% proof strength (MPa) (O) (H111)
|
35
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rp0.2 0.2% proof strength (MPa) (F) (H112)
|
35
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A - Min. elongation at fracture (%) (H12)
|
8
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A - Min. elongation at fracture (%) (H14)
|
5
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A - Min. elongation at fracture (%) (O) (H111)
|
25
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A - Min. elongation at fracture (%) (F) (H112)
|
25
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A - Min. elongation Lo = 50mm (%) (H12)
|
3月7日
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A - Min. elongation Lo = 50mm (%) (H14)
|
2月5日
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A - Min. elongation Lo = 50mm (%) (O) (H111)
|
20
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A - Min. elongation Lo = 50mm (%) (F) (H112)
|
20
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Brinell hardness (HBW): (O) (H111)
|
30
|
|
|
|
|
|
|
Brinell hardness (HBW): (F) (H112)
|
30
|
|
|
|
|
|
|
Brinell hardness (HBW): (O)
|
28 - 33
|
|
|
|
|
|
|
Brinell hardness (HBW): (H12)
|
38
|
|
|
|
|
|
|
Brinell hardness (HBW): (H12)
|
46
|
|
|
|
|
|