2017A 鋁合金。薄板、帶材
|
|
|
|
|
|
|
|
|
編號(hào):ENAW-2017A
|
|
|
|
|
|
|
|
|
分類:鋁-2000系列(銅是主要合金元素)
|
|
|
|
|
|
|
|
|
標(biāo)準(zhǔn):EN 573-3:2009鋁和鋁合金。鍛造產(chǎn)品的化學(xué)成分和形式。產(chǎn)品的化學(xué)成分和形式
|
|
|
|
|
|
|
|
|
EN 755-2:2008鋁和鋁合金。擠壓棒材、管材和型材。機(jī)械性能
|
|
|
|
|
|
|
|
|
EN 485-2:2008鋁和鋁合金。薄板、帶材和板材。機(jī)械性能
|
|
|
|
|
|
|
|
|
EN 754-2:2008鋁和鋁合金。冷拔棒材/棒材和管材。機(jī)械性能
|
|
|
|
|
|
|
|
|
EN 1301-2:1997鋁和鋁合金。拉線。機(jī)械性能
|
|
|
|
|
|
|
|
|
EN 941:1996鋁和鋁合金。用于一般應(yīng)用的圓形和圓形坯料。規(guī)格
|
|
|
|
|
|
|
|
|
EN 12392:2000鋁和鋁合金。鍛造產(chǎn)品。壓力設(shè)備生產(chǎn)用產(chǎn)品的特殊要求
|
|
|
|
|
|
|
|
|
EN 1715-3:2008鋁和鋁合金。提取庫存。機(jī)械用途的具體要求(不包括焊接)
|
|
|
|
|
|
|
|
|
Chemical comb % of grade 2017A
|
|
|
|
|
|
|
|
|
Fe
|
Si
|
Mn
|
Cr
|
Cu
|
Mg
|
Zn
|
Others
|
-
|
max 0.7
|
0.2 - 0.8
|
0.4 - 1
|
max 0.1
|
3.5 - 4.5
|
0.4 - 1
|
max 0.25
|
each 0.05; total 0.15
|
Zr+Ti < 0.25; Al - remainder
|
|
|
|
|
|
|
|
|
|
Mechanical properties of grade 2017A
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rm - Tensile strength (MPa) (O)
|
225
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rm - Tensile strength (MPa) (0) (H111)
|
250
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rm - Tensile strength (MPa) (T4)
|
360-400
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rp0.2 0.2% proof strength (MPa) (O)
|
145
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rp0.2 0.2% proof strength (MPa) (0) (H111)
|
135
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rp0.2 0.2% proof strength (MPa) (T4)
|
220-270
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A - Min. elongation at fracture (%) (O) (H111)
|
12
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A - Min. elongation at fracture (%) (T4)
|
7月12日
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A - Min. elongation Lo = 50mm (%) (O)
|
12月14日
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A - Min. elongation Lo = 50mm (%) (O) (H111)
|
10
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A - Min. elongation Lo = 50mm (%) (T4)
|
8月10日
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Brinell hardness (HBW): (O) (H111)
|
45
|
|
|
|
|
|
|
|
Brinell hardness (HBW): (T4)
|
105
|
|
|
|
|
|
|
|
Brinell hardness (HBW): (O)
|
55
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|